Over the last 50 years, Australia has become a major producer of bauxite ore and a major producer and exporter of alumina.[21] Australia produced 62 million tonnes of bauxite in 2005. The Australian deposits have some refining problems, some being high in silica but have the advantage of being shallow and relatively easy to mine.[22]

Aluminium is a strongly reactive metal that forms a high-energy chemical bond with oxygen. Compared to most other metals, it is difficult to extract from ore, such as bauxite, due to the energy required to reduce aluminium oxide (Al2O3). For example, direct reduction with carbon, as is used to produce iron, is not chemically possible, since aluminium is a stronger reducing agent than carbon. However there is an indirect carbothermic reduction possible by using carbon and Al2O3 which forms an intermediate Al4C3 and this can further yield aluminum metal at a temperature of 1900-2000°C. This process is still under development. This process costs less energy and yields less CO2 than the Hall-Heroult process.[18] Aluminium oxide has a melting point of about 2,000 °C. Therefore, it must be extracted by electrolysis. In this process, the aluminium oxide is dissolved in molten cryolite and then reduced to the pure metal. The operational temperature of the reduction cells is around 950 to 980 °C. Cryolite is found as a mineral in Greenland, but in industrial use it has been replaced by a synthetic substance. Cryolite is a chemical compound of aluminium, sodium, and calcium fluorides: (Na3AlF6). The aluminium oxide (a white powder) is obtained by refining bauxite in the Bayer process of Karl Bayer. (Previously, the Deville process was the predominant refining technology.)

The electrolytic process replaced the Wohler process, which involved the reduction of anhydrous aluminium chloride with potassium. Both of the electrodes used in the electrolysis of aluminium oxide are carbon. Once the refined alumina is dissolved in the electrolyte, its ions are free to move around. The reaction at the cathode is:

Al3+ + 3 e? > Al

Here the aluminium ion is being reduced. The aluminium metal then sinks to the bottom and is tapped off, usually cast into large blocks called aluminium billets for further processing.

At the anode, oxygen is formed:

2 O2? > O2 + 4 e?

This carbon anode is then oxidized by the oxygen, releasing carbon dioxide:

O2 + C > CO2

The anodes in a reduction cell must therefore be replaced regularly, since they are consumed in the process.

Unlike the anodes, the cathodes are not oxidized because there is no oxygen present, as the carbon cathodes are protected by the liquid aluminium inside the cells. Nevertheless, cathodes do erode, mainly due to electrochemical processes and metal movement. After five to ten years, depending on the current used in the electrolysis, a cell has to be rebuilt because of cathode wear.

World production trend of aluminiumAluminium electrolysis with the Hall-Heroult process consumes a lot of energy, but alternative processes were always found to be less viable economically and/or ecologically. The worldwide average specific energy consumption is approximately 15±0.5 kilowatt-hours per kilogram of aluminium produced (52 to 56 MJ/kg). The most modern smelters achieve approximately 12.8 kW·h/kg (46.1 MJ/kg). (Compare this to the heat of reaction, 31 MJ/kg, and the Gibbs free energy of reaction, 29 MJ/kg.) Reduction line currents for older technologies are typically 100 to 200 kA; state-of-the-art smelters[19] operate at about 350 kA. Trials have been reported with 500 kA cells.

Electric power represents about 20% to 40% of the cost of producing aluminium, depending on the location of the smelter. Smelters tend to be situated where electric power is both plentiful and inexpensive, such as South Africa, Ghana, the South Island of New Zealand, Australia, the People's Republic of China, the Middle East, Russia, Quebec and British Columbia in Canada, and Iceland.[20]

Aluminium output in 2005In 2005, the People's Republic of China was the top producer of aluminium with almost a one-fifth world share, followed by Russia, Canada, and the USA, reports the British Geological Survey.

Over the last 50 years, Australia has become a major producer of bauxite ore and a major producer and exporter of alumina.[21] Australia produced 62 million tonnes of bauxite in 2005. The Australian deposits have some refining problems, some being high in silica but have the advantage of being shallow and relatively easy to mine.[22]

6. Recycling

Aluminium is 100% recyclable without any loss of its natural qualities. Recovery of the metal via recycling has become an important facet of the aluminium industry.

Recycling involves melting the scrap, a process that requires only five percent of the energy used to produce aluminium from ore. However, a significant part (up to 15% of the input material) is lost as dross (ash-like oxide).[23]

Recycling was a low-profile activity until the late 1960s, when the growing use of aluminium beverage cans brought it to the public awareness.

In Europe aluminium experiences high rates of recycling, ranging from 42% of beverage cans, 85% of construction materials and 95% of transport vehicles.[24]

Recycled aluminium is known as secondary aluminium, but maintains the same physical properties as primary aluminium. Secondary aluminium is produced in a wide range of formats and is employed in 80% of the alloy injections. Another important use is for extrusion.

White dross from primary aluminium production and from secondary recycling operations still contains useful quantities of aluminium which can be extracted industrially.[25] The process produces aluminium billets, together with a highly complex waste material. This waste is difficult to manage. It reacts with water, releasing a mixture of gases (including, among others, hydrogen, acetylene, and ammonia) which spontaneously ignites on contact with air;[26] contact with damp air results in the release of copious quantities of ammonia gas. Despite these difficulties, however, the waste has found use as a filler in asphalt and concrete.[27]

7. Chemistry

7.1 Oxidation state +1

AlH is produced when aluminium is heated in an atmosphere of hydrogen. Al2O is made by heating the normal oxide, Al2O3, with silicon at 1800 °C in a vacuum.[28]

Al2S can be made by heating Al2S3 with aluminium shavings at 1300 °C in a vacuum.[28] It quickly disproportionates to the starting materials. The selenide is made in a parallel manner.

AlF, AlCl and AlBr exist in the gaseous phase when the tri-halide is heated with aluminium. Aluminium halides usually exist in the form AlX3, where X is F, Cl, Br, or I.[28]

7.2 Oxidation state +2

Aluminium monoxide, AlO, has been detected in the gas phase after explosion[29] and in stellar absorption spectra.[30]

7.3 Oxidation state +3

Fajans' rules show that the simple trivalent cation Al3+ is not expected to be found in anhydrous salts or binary compounds such as Al2O3. The hydroxide is a weak base and aluminium salts of weak acids, such as carbonate, cannot be prepared. The salts of strong acids, such as nitrate, are stable and soluble in water, forming hydrates with at least six molecules of water of crystallization.

Aluminium hydride, (AlH3)n, can be produced from trimethylaluminium and an excess of hydrogen. It burns explosively in air. It can also be prepared by the action of aluminium chloride on lithium hydride in ether solution, but cannot be isolated free from the solvent. Alumino-hydrides of the most electropositive elements are known, the most useful being lithium aluminium hydride, Li[AlH4]. It decomposes into lithium hydride, aluminium and hydrogen when heated, and is hydrolysed by water. It has many uses in organic chemistry, particularly as a reducing agent. The aluminohalides have a similar structure.

Aluminium hydroxide may be prepared as a gelatinous precipitate by adding ammonia to an aqueous solution of an aluminium salt. It is amphoteric, being both a very weak acid, and forming aluminates with alkalis. It exists in various crystalline forms.

Aluminium carbide, Al4C3 is made by heating a mixture of the elements above 1000 °C. The pale yellow crystals have a complex lattice structure, and react with water or dilute acids to give methane. The acetylide, Al2(C2)3, is made by passing acetylene over heated aluminium.

Aluminium nitride, AlN, can be made from the elements at 800 °C. It is hydrolysed by water to form ammonia and aluminium hydroxide. Aluminium phosphide, AlP, is made similarly, and hydrolyses to give phosphine.

Aluminium oxide, Al2O3, occurs naturally as corundum, and can be made by burning aluminium in oxygen or by heating the hydroxide, nitrate or sulfate. As a gemstone, its hardness is only exceeded by diamond, boron nitride, and carborundum. It is almost insoluble in water. Aluminium sulfide, Al2S3, may be prepared by passing hydrogen sulfide over aluminium powder. It is polymorphic.

Aluminium iodide, AlI3, is a dimer with applications in organic synthesis. Aluminium fluoride, AlF3, is made by treating the hydroxide with HF, or can be made from the elements. It consists of a giant molecule which sublimes without melting at 1291 °C. It is very inert. The other trihalides are dimeric, having a bridge-like structure.

When aluminium and fluoride are together in aqueous solution, they readily form complex ions such as [AlF(H2O)5]2+, AlF3(H2O)3, and [AlF6]3?. Of these, [AlF6]3? is the most stable. This is explained by the fact that aluminium and fluoride, which are both very compact ions, fit together just right to form the octahedral aluminium hexafluoride complex. When aluminium and fluoride are together in water in a 1:6 molar ratio, [AlF6]3? is the most common form, even in rather low concentrations.

Organometallic compounds of empirical formula AlR3 exist and, if not also polymers, are at least dimers or trimers. They have some uses in organic synthesis, for instance trimethylaluminium.

7.4 Analysis

The presence of aluminium can be detected in qualitative analysis using aluminon.

8. Applications

8.1 General use

Aluminium is the most widely used non-ferrous metal.[31] Global production of aluminium in 2005 was 31.9 million tonnes. It exceeded that of any other metal except iron (837.5 million tonnes).[32] Relatively pure aluminium is encountered only when corrosion resistance and/or workability is more important than strength or hardness. A thin layer of aluminium can be deposited onto a flat surface by physical vapour deposition or (very infrequently) chemical vapour deposition or other chemical means to form optical coatings and mirrors. When so deposited, a fresh, pure aluminium film serves as a good reflector (approximately 92%) of visible light and an excellent reflector (as much as 98%) of medium and far infrared radiation.

Pure aluminium has a low tensile strength, but when combined with thermo-mechanical processing, aluminium alloys display a marked improvement in mechanical properties, especially when tempered. Aluminium alloys form vital components of aircraft and rockets as a result of their high strength-to-weight ratio. Aluminium readily forms alloys with many elements such as copper, zinc, magnesium, manganese and silicon (e.g., duralumin). Today, almost all bulk metal materials that are referred to loosely as "aluminium," are actually alloys. For example, the common aluminium foils are alloys of 92% to 99% aluminium.[33]

Some of the many uses for aluminium metal are in:

Transportation (automobiles, aircraft, trucks, railway cars, marine vessels, bicycles etc.) as sheet, tube, castings etc.

Packaging (cans, foil, etc.)

Construction (windows, doors, siding, building wire, etc.)

A wide range of household items, from cooking utensils to baseball bats, watches.[34]

Street lighting poles, sailing ship masts, walking poles etc.

Outer shells of consumer electronics, also cases for equipment e.g. photographic equipment.

Electrical transmission lines for power distribution

MKM steel and Alnico magnets

Super purity aluminium (SPA, 99.980% to 99.999% Al), used in electronics and CDs.

Heat sinks for electronic appliances such as transistors and CPUs.

Substrate material of metal-core copper clad laminates used in high brightness LED lighting.

Powdered aluminium is used in paint, and in pyrotechnics such as solid rocket fuels and thermite.

8.2 Aluminium compounds

Aluminium ammonium sulfate ([Al(NH4)](SO4)2), ammonium alum is used as a mordant, in water purification and sewage treatment, in paper production, as a food additive, and in leather tanning.